1.Introduction

Electron beam welding(EBW),an autogenous and high power density fusion welding process,is extensively employed in aerospace and defence applications as it offers ample advantages over other conventional arc welding processes.EBW produces weld beads with high depth-to-width ratios,thus,minimizing heat input associated detrimental effects on weld performance[1,2].As the EBW process is performed in vacuum conditions,fusion related weld defects are,in general,less in electron beam welds as compared to arc welding processes.As reported by Metzer and Lison[3],the electron beam welding has certain unique characteristics such as ability to produce narrow fusion zone with minimum dilution of base materials,ease of precisely locating weld joint etc.make this process as the better choice for fusion welding of dissimilar metals.The serviceability of welded joints mainly depends on shape and size of weld bead and constituent microstructures.By adopting the aforeentioned special characteristics of the EBW process,it is extensively explored in fusion welding of wide variety of dissimilar metals and alloys[Sun and Karppi[4]].

2.State-of-the-art

In general,the weld bead geometry in thick EBW is peculiarkind of a ‘nail headed’,as shown in Fig.1.It is dif ficult to envisage that geometric parameters widely used to de fine weld bead geometry in other autogenous process like Tungsten inert gas(TIG)welding-top bead width(TW),top depression(TD),bottom penetration(BP),and bottom bead width(BW)[Sharma et al.[5]]would effectively explain the behavior of EBW welds.The top and bottom portions of the ‘nail headed’weld bead are due to different phenomena at surface and inside the body of the workpiece which need to be modelled as a two heat source problem[Klykov et al.[6]].

Therefore very limited investigations are reported for prediction of weld bead geometry shape of EB welds,as shown inTable 1.Most of these works have concentrated on regression analysis or statistical modelling of weld bead geometry,heat affected zone(HAZ)width or in few studies,and joint strength of similar material combinations.Welding of dissimilar alloys deserve more care and attention as compared to that of similar materials.More so,the weld bead geometry of dissimilar alloys depend on physical and thermal properties of dissimilar base materials and joint strength is also affected by bead geometry as well as the welding parameters.

轩辕明在神像旁边发现了一个木牌，木牌上标着：南方第二列山系，从柜山到此漆吴山共十七座山，共长七千二百里。

The present work assumes special significance since no research article is found,to the best of authors'knowledge,in the open literature in which weld bead geometry and its effect on weldmechanical properties pertaining to dissimilar aluminium alloy electron beam weldsare investigated.The alloy combination considered in this investigation is a prominent in aerospace and defence applications.AA2219 aluminium alloy is widely used in manufacturing of airframes,fuel tanks due to its high strength while AA5083 aluminium alloy is employed in pipe lines,external walls of naval sub systems because of its corrosion resistance properties.However in certain applications where some part of subsystem require high strength while the other component may demand for better corrosion resistance,the dissimilar welding between AA2219 and AA5083 aluminium alloys is highly useful.The present work focuses on developing relationship between the weld bead geometry and tensile breakingloadofdissimilaraluminium alloy(AA2219and AA5083)electron beam weld joint.A regression model is developed wherein breaking load is mapped as a function of weld bead geometry.The developed equations are validated through test experiments and further the weld joint strength is correlated to microstructures and distribution of alloying elements in fusion and heat affected zones.

本岛气候比较特殊4～11月为雨季、5～10月为旱季，雨季期间早晚温度与中午温差较大，差值为20～30℃，旱季温差较小5～10℃，鉴于上述情况，为了更好地控制焊接质量，雨季施工期间由于环境温度的变化采用厂家提供的参数不能更好地满足质量的要求，在此期间需要分时段调整不同焊接电压来满足管材与管件所要吸收的热量，即雨季采用THE-9C焊机焊接更能满足质量的要求。旱季温差变化不大，采用HTA-3B单时段单参数熔接，靠自身的温差补偿可满足焊接质量要求，并且也可以减少人为操作出现的错误。

3.Experimental work

The base materials employed in the present research were AA2219-T6 Al-Cu alloy and AA5083-H116 Al-Mg alloy.The analyzed chemical compositions and mechanical properties of base materials are listed in Table 2.The width of weld coupon was maintained along the rolling direction.Electron beam welding of 75 mmwidth x 125 mm length x 5 mm thickness plates was carried out in square butt joint con figuration after positioning and firmly clamping the plates on a CNC work table.The selected welding process parameters that are considered in this study are accelerating voltage(V)in kV,beam current(I)in mA,welding speed(s)in mm/min.Remaining welding conditions such as vacuum level in welding chamber(1×10-4mbar),electron gun to work piece distance,focus position and pre-weld cleaning procedures are maintained as constant throughout the experimentation.

Electron beam welding trials were carried out in a CNC controlled low kV electron beam welding machine of M/s.TECHMETA make.The experiments were planned and conducted as per Taguchi method using a L25 orthogonal array with three-factors and each factor with five-levels.The gun to work distance is kept constant at 240mm.The minimum and maximum operating levels of each welding parameter were decided based upon prior experience and after conducting certain pilot experimental bead on trials.Feasible limits of the each parameter was selected in such a way that the resulting electron beam welded joints would have uniform thread-like bottom penetration.The Table 3 shows the number of welding experimental runs and corresponding welding parameters as per L25 orthogonal array.

The weld joints were initially visually inspected and further subjected to X-ray radiography to inspect for the presence of various internal and surface defects.The weld macrostructures of transverse section were examined under optical metallurgical microscope,after standard metallographic sample preparation using modified Keller's reagent.The weld macrostructures were analyzed to measure different weld bead geometrical features such as top bead width(TW),top depression(TD),bottom penetration(BP)and bottom bead width(BW).The welding parameters and measured weld bead geometry features are given in Table 3.

The weld bead geometrical parameters are interdependent.The interdependence is shown in Fig.5.With the change in process conditions that enhance the heat input the volume of molten metal increases,in turn the weld width widens along with deepening of top depression,increase of bottom penetration,and increase in bottom width.However,excess widening of weld width spreads the heat over larger area that reduces the top depression and bottom weld width,as observed in Fig.5.However the molten metal along the center core of the beam increases due to increase in heat input responsible for increasing the weld width.

The tensile test specimens were extracted along the transverse direction of the weld joint such that the specimen geometry conforms to the standard ASTM E8.The room temperature tensile properties of three specimens for each experiment were evaluated in as-welded condition,without machining top depression or penetration,on a universal tensile testing machine of INSTRON make at a crosshead speed of 1mm/min.A mathematical model was developed using regression analysis-as explained later-for prediction of tensile breaking load of weld joint as a function of weld bead geometrical features.The microhardness was measured using Vickers microhardness tester at 100 gf load.The micro hardnessindentationswerespacedwith 0.25mm intervals covering various zones of weldments and base materials across the mid thickness of the transverse weld cross section.Face bend testing of weld joint was carried out as per standard ASTM E190.The fractured surfaces of tensile test specimens are examined under ZEISS make scanning electron microscope at an accelerating voltage of 20 kV in order to understand the mode of failure and for the presence of any inter-metallic compound particles on thesefracture surfaces.

4.Development of regression model

The breakingstrength of a weld bead joint depends on the weld bead geometry and the microstructure of the weld metal and head affected zone.The relation between shape and size of the weld and breaking strength,which is not more often reported,is an important step to understand the weld bead formation and its in fluence on weld strength.The response parameter representing the tensile breaking load(TBL)of dissimilar electron beam weld joints as a function of weld bead geometrical parameters may be expressed as

The effective weld thickness Teis as

A regression equation is developed using stepwise regression method using MINITAB version 17.Details of this method can be elsewhere[13].The deduced second order polynomial regression equation after incorporating all the values of the regression coefficients is as follows:

After initiation fracture,the crack has propagated through the fusion interface of AA5083 alloy side,as this zone has reported minimum hardness region as compared to all the other regions of dissimilar weldment,which was in turn a resultant of loss of cold working or softening because of exposure to high temperatures caused due to welding heat.A similar observations are reported by Yamaguchi et al.[17],Cam et al.[19]and Oladimeji et al.[23].

The tensile test is conducted with a goal to estimate the load bearing capacity of weld joint in as-welded condition without any post weld machining operations.As the test specimens are not machined or ground after welding,the thickness of the flat transverse tensile test was noticed to be varying beyond acceptable limits as specified bywidely practiced standard of tensile testingi.e,ASTM E8.So testing of tensile specimens,without machining top depression and penetration of the weld joint,has prompted localizing the tensile fracture in fusion zone.So,it was considered to evaluate tensile breaking load and displacement in 25 mm gauge length for weld joints instead of usual tensile strength,yield strength and elongations which are dependent of cross sectional area of test specimen.The transverse tensile properties of EB weld joints and the corresponding AA2219 and AA5083 alloy base materials are mentioned in Table 5.Load versus displacement curves for both base materials and weld joint are presented in Fig.17.

The adequacy of the regression model is judged by the analysis of variance(ANOVA),as shown in Table 4.It is observed that the calculated F-ratio is higher than the tabulated F-ratio at con fidence level more than the 95%.So,the developed model is considered to be adequate and predicts the response without appreciable error.

The model was developed using 21 out of 25 observations and rest four were used to con firm the model.The predicted error for both the development and con firmation data is found within±10%band as shown in Fig.2.The coefficients of determination for the mode R2,R2(adj),and R2(pred)for the observed results are 99.73%,99.67%,and 99.58%,respectively that shows that the developed model is adequate and can predict the response without appreciable error.

“海洋石油982”深水半潜式钻井平台是中海油田服务股份有限公司自主投资建造的第一座深水半潜式钻井平台。该平台属第六代钻井平台，配备了世界最先进的DP3动力定位系统和NOV钻井系统，采用全球最先进的能源管理和绿色设计理念，拥有智能变频、余热淡化等多项先进技术，具备1500米水深海域进行油气勘探开发作业的能力。

5.Results and discussion

5.1.Weld appearance and bead geometry

The appearance of top and bottom side of a typical weld bead joint and the corresponding X-ray radiograph is shown in Fig.3.The weld joints are noticed to have a depression in fusion zone on top side and a positive penetration at bottom side.X-ray radiograph of weld joint reveals presence of no significant defect.

在重塑沟通的过程中，媒介融合从技术层面应体现为一种全息感知系统模式，这种模式通过传播介质与内容和各媒介的组织结构层次的融合日常化地嵌合在人们感知信息节点上，在整个社会系统中汇聚、流通，媒介组织（媒体）只是其中的一个节点。随着2014年后国家从顶层设计的政治逻辑对于媒体融合的指导作用愈加强大，如何以人为本构建与用户的连接平台，以用户数据为依据实现内容产业跨界合作、用户人脉关系再造和地方社会动员，避免区域各媒体间虚假的团结，打造互联网上真正敞开技术、内容、资源、渠道交流的平台，才是目前该思考的出路。

The macrostructures of all the dissimilar aluminium alloy electron beam weld cross sections produced with different process parameters is presented in Fig.4.It can be deduced that it is possible to produce defect free weld joints with accelerating voltage 40-60 kV,beam current 35-55 mA and welding speed 800-1200 mm/min.All the weld joints are noticed to be free from bulk porosity but there exists varied weld bead geometries with changes in welding parameters.The weld bead width and top depression is observed to be increasing with increase in welding heat input.Overall view of all the weld bead cross sections reveal presence of certain amount of depression of weld bead zone from top surface and positive penetration is noticed in almost all the weld joints.

5.2.Relationship in between weld bead geometry and weld strength

综上所述，本文分析了蓝牙技术在航标上的应用，通过在航标灯上引入蓝牙技术，可以减少在恶劣海况下巡检的危险性，降低巡检维护的成本，给巡检维护的工作人员提供了必要的帮助，有助于提高航标维护管理水平，为经过该区域的船舶提供更加优质的导助航服务。

The bead geometry in fluences the weld strength.The relationship between weld bead geometry and breaking load is obtained using simulation of the functional relation in Eq.(4)and shown in Fig.6.It can be seen that with increase in top depression,bottom penetration,and bottom weld width,the breaking load decreases while the process parameters responsible for wider top weld width increases the breaking load.The widening of weld width reduces the top depression at the same time helps to improve bottom penetration.This helps toincrease the totaleffectiveweld thickness Te.The increase in Te increase the weld strength that also corroborates frompositive coefficientof Tein Eq.(3).Along with the weld bead microstructures-that itself may be affected by weld geometry due to change in heating and cooling rates-also impacts the weld strength as described next.

High magnification microstructures of AA5083 base material and its corresponding heat affected zone are shown in Fig.12(a)&(b)respectively.The distribution of grain size in base material and HAZ of AA5083alloyare also measured and plotted(Fig.13(a)&(b))using planimetric method It is clearly evident from these microstructures and plots that there is very little variation in the grain size of the HAZ as compared to that of base material of AA5083 alloy.This could be primarily due to the prevailing lower welding heat inputs,faster cooling rates and lesser thermal diffusivity of AA5083 alloy.

The macrostructures of two typical weld joints are shown in Fig.7 The macrostructure in Fig.7(a)depicts a weld bead geometry with certain degree of uniformity with minimum amount of top depression and bottom penetration is noticed.Whereas the macrostructure of weld joint shown in Fig.7(b)has relatively highest amount of top depression with an uneven weld bead geometry.

5.3.Microstructural analysis

The optical microstructures of the base materials,AA2219-T6and AA5083-H116 aluminum alloys are shown in Fig.8.The AA2219 base material consists of typical coarse grains measuring approximately to1.5-2.0mm with presenceθ(CuAl2)particles spread across the whole matrix both at grain boundaries and interior to the grains.

Precipitation sequence,as mentioned by Li and Schen[14],in a supersaturated solid solution of AA2219 aluminum alloy is as mentioned below

where,αisa solid solution of Cu in Al matrix,GP zones are Guinier-Preston zones.After precipitation hardening or ageing,the alloy attains higher strength due to the impediment of dislocations by θ′′and θ′precipitates.However,the θ-particle is an inter-metallic compound(CuAl2)which stays incoherent to theα-matrix.The microstructure(Fig.8(b))of AA5083 base material contains uniformly distributed fine grain size with slightly elongated grains in the direction of rolling.It is further observed from Fig.13(a)that the maximum population of grains in AA5083 base material found to be varying from ASTM grain size number from 10 to 12.

The microstructures of differentzones of a typical electron beam welded joint are shown in Fig.9.The different zones of weld crosssection are marked from b-i.The base metal of AA2219 alloy has coarse as-forged grains as it is seen from Fig.9(b).The microstructures close to AA 2219 interface is shown in Fig.9(c).The interface near AA 2219 alloy side is very clear and distinct,from which the fusion zone grains are noticed to be originated.The grain size in the fusion zone(Fig.9(e)&(f))is observed to be very fine and is typically smaller by few orders as compared to that of AA 2219 alloy base material.The fine grain size in fusion zone is the result of faster cooling rates prevailing in the key hole mode welding that happens during electron beam welding process.Similar observations on grain size in fusion zone are made by Yanbin et al.[15]and Nair et al.[16].

The optical microstructures near the both fusion interfaces and fusion zone at higher magnifications are shown in Fig.10.The fusion zone is found to have primarily very fine columnar dendrites originating from the fusion interface(See Fig.10(a)).The central part of fusion zone consists of equiaxed fine grains(as shown in Fig.10(b))which are formed due to faster cooling rate that exist during welding.The interface of fusion zone towards AA5083 alloy side is shown in Fig.10(c)and(d).The fusion interface near AA5083 alloy is found to be more diffused over a wide area while the interface at AA2219 alloy side is found to be a sharp line(Fig.10(a))that is clearly distinct.This phenomenon is due to the fact that the thermal diffusivity of AA 5083 alloy(0.45cm2/s)is smaller than that of AA2219 alloy(0.5 cm2/s)which causes major portion of welding heat gets accumulated at the fusion interface of AA5083 alloy instead of getting transferred to the heat affected zone or base material.

The optical microstructures given in Fig.11(a)depicts presence of eutectic phase(θ-particles)spread along the grain boundaries of super saturated Al-Cu solid solution in AA2219 aluminium alloy.Upon exposure to the severe welding thermal cycles,re-melting of this prior existing eutectic phase occurs as it is the last to solidify.The grain boundaries close to the fusion interface experience higher degree of temperatures during welding time and these zones are generally very narrow in high energy density welds,mostly covering width of one or two grains.Fig.11(b)clearly indicate eutectic re-melting at the fusion interface near AA2219 alloy side.

（3）排除故障后，闭合开关，电压表示数为1V，小灯泡实际亮度偏____（选填“亮”或“暗”）；为了使小灯泡正常发光，则滑动变阻器滑片应向________移动（选填“C”或“D”）。

多年来，很少有贪官是通过《党政领导干部收入申报规定》和《党政领导干部考核暂行规定》被发现的。因此，在落实相关条例规定时，要增加审核、公示、考核、惩治等环节内容。《国家公职人员行为道德典》以近年来出台的一批党规为制定根据，提升至道德层面约束官员。《国家公职人员腐败犯罪惩治条例》则应该以近年来“两院”出台的司法解释为基础制定。［8］

Many researchers[15,17,18]have reported that the evaporation of major alloying elements during high energy density welding of aluminium alloys.Inparticular,during laser/electron beamwelding of 5xxx aluminium alloys,earlier studies have reported evaporation losses of%Mg even to the extent of 10-20%[19].In order to understand the composition of existing alloying elements in fusion zone of this dissimilar electron beam weld,EDAX analysis is carried out and the results of area and point analysis are given in Figs.14 and 15.It is noticed from the results of EDAX area analysis given in Fig.that the magnesium is evaporated from the top of fusion zone by 20.2%due to the keyhole mode welding because Mg has low vaporization temperature.In this zone,in addition to 3.35wt%of magnesium,presence of copper is measured as 3.21 wt%which indicates that the suf ficient dilution of AA2219 alloy and AA5083 alloy in fusion zone.The wt%of measured copper in this zone is lower than that of AA2219 base material which could be due to the fact that copper segregation in fusion zone.However the EDAX point analysis(Fig.15)in the fusion zone indicates that iron is segregated in fusion zone.Presence of iron along with copper and magnesium in aluminium matrix may lead to formation of fine inter-metallic compounds or precipitates like Al2CuMg,Al15Fe3Si etc.

5.4.Microhardness survey

The typical variation of microhardness along the mid thickness of transverse cross section across the dissimilar electron beamweld is shown in Fig.16.The hardness of AA2219 base material was substantially higher than that of AA5083 base material.As can be seen,there was a drop in the hardness in the HAZ close to AA2219 alloy as compared to the un-affected AA2219 base material.A similar trend was observed in HAZ towards AA5083 alloy side as compared to the unaffected AA5083 alloy base material.The hardness of fusion zone was found to be significantly lower than that of AA2219 base material and slightly higher than the AA5083 base material.The reduction in hardness in HAZ of AA2219 alloy side could be due to dissolution or coarsening of Al2Cu precipitates due to the exposure to welding heat input.Fusion zone hardness is less than that of AA2219 alloy base material due to complete dissolution strengthening precipitates in fusion zone.Similarly the drop in hardness of HAZ of AA 5083 alloy side can be correlated to the loss of cold working/softening due to decreased dislocation density during EB welding process.Yan-bin et al.[15],Cam et al.[19],Cam et al.[20]and Mastanaiah et al.[21]have reported reduction of hardness in HAZ of different types 5xxx aluminum alloys.

在考虑已明确电源基础上，根据电力电量平衡计算结果，2025年广东电力缺口约3 GW。根据《广东省能源发展“十三五”规划》，广东开工建设湛江核电一期2×1 250 MW机组；再考虑新增部分新能源装机，预计2025年广东无电力缺额。

1.6 统计学分析 本研究所得数据均采用SPSS 21.0软件进行统计，计数资料采用率表示，用χ2检验，计量资料以（±s）表示，采用t检验，P＜0.05为差异有统计学意义。

5.5.Tensile test results

宋彬还谈到了目前新三板企业IPO的审核排队情况。他说，截至2018年9月30日，处于IPO正常审核状态的首发企业共264家，其中新三板企业共60家（含已摘牌新三板企业），占比22.73%；新三板企业中已通过发审会企业7家，已暂缓表决企业1家，已预先披露更新企业35家，已反馈企业13家，已受理企业4家。

The model is further simulated tounderstand the relationship in between the weld bead geometry and weld strength as presented next.Subsequently the results are corroborated with microstructural observations.

One can easily deduce from Fig.17 that the dissimilar weld joint possess the tensile breaking loadmoderately higher than AA5083 alloy base material and less than that of AA2219 alloy base material.The weld specimen has demonstrated better ductility than the specimen of AA2219 alloy base material and slightly lesser than the AA5083 alloy base material.Optical macrograph of the fractured tensile test specimen of weld joints is shown in Fig.18.It is clearly evident from Fig.18(a)that the fracture of weld joint has initiated from centre of top depression and the crack has propagated through the fusion interface of AA5083 alloy side which posses minimum hardness compared to the other zones of weld joint(Fig.16).

It is noticed that the weld joint fracture was initiated at top of the fusion zone which could be due to stress concentration effect aroused from the profound variations in the weld bead geometry.Top depression of the weld joint has lead to the stress concentration and localization of fracture in fusion zone.Another reason for initiation of crack at the fusion zone could be due to the depletion of major alloying element magnesium from the fusion zone,which was aided by evaporation of magnesium during keyhole mode electron beam welding.Punkari et al.[18]and Cam et al.[19]have reported loss of magnesium from power beam welding processed weld zones by around 10-20%.They also found out that loss of magnesium is one of the major reasons for the fracture initiation at fusion zone of high energy density welding joints of 5xxx aluminium alloys.

However,the dissimilar electron beam weld joint which was welded with parameters 55 kV,35mA and 1100 mm/min has shown highest breaking load among all the weld joints.This breaking load is slightly higher tensile breaking load than that of AA5083 alloy base material.One reason for the higher tensile breaking load of weld joint is due to higher effective thickness(5.23mm,as shown in Fig.17)of weld bead which was resulted from the particular welding parameters.In this case,bottom penetration is more than top depression, finally resulting in effective thickness of 5.23mm as against the base material thickness of 5mm.The measured top depression in this particular weld bead geometry suggests that the increase in the breaking load of the dissimilar weld joint as compared to the AA5083 base material could be due to the presence of localized notch like top depression.The presence of notch in a tensile specimen under uni-axial load introduces three effects[22].(i)There is an increase or concentration of stress at the root of the notch(ii)A tri-axial state of stress is produced at notch(iii)A stress gradient is setup from the root of the notch towards the centre of the specimen.Hence,it is understood that the breaking load of this weld joint is slightly more than that of the AA5083 alloy base material.

The other dissimilar weld joint which was welded with parameters 55 kV,45 mA and 800mm/min has demonstrated lowest breaking load among all the weld joints.The ductility of this weld joint possesses lower ductility as compared to other welds.So,the weld is observed to have both breaking load and displacement lower than those of other weld joints.

For the present case T=5mm,thus Eq.(3)can be rewritten using Eq.(2)as follows

5.6.Fractography

The scanning electron microscope(SEM)images of fractured surfaces of tensile test specimens of weld joint of highest breaking load are shown in Fig.19.The fractographs shown in Fig.19(b)&(c)correspond to the fusion zone and interface on AA5083 alloy side.Fractographs of both the zones primarily portray fine elongated dimples which con firm that fracture has predominantly occurred in ductile mode.

2.1 岸边环境污染 消落带是物质能量输送与转化的活跃地带，库岸的生活及工业垃圾、农作物残留化肥农药等污染物直接进入水体，导致水体污染和富营养化，加上消落区域缺乏固有植被的拦截过滤，自净能力低下，极容易形成岸边水陆交叉污染带。

Fine dimples are characteristic feature of ductile material.The weld joint produced with welding parameters 55 kV,35mA and 1100 mm/min has shown highest tensile breaking load and displacement as compared to the welds produced with parameters 55 kV,45 mA and 800mm/min and to other weld joints.The dimple size exhibits a directly proportional relationship with tensile breaking load and displacement i.e.,if the dimple size is finer,then the tensile breaking load and ductility of the respective weld joint is higher or vice versa.

The scanning electron microscope(SEM)images of fractured surfaces of tensile test specimens of weld joint of lowest breaking load are shown in Fig.20.The fractographs presented in Fig.20(b),(c)&(d)suggests that occasional cleavage like features are evident in the grain interiors in addition to the micro void features.The fracture of this particular weld joint appears to be shear dominated phenomenon.The sheared regions were oriented ～45°to the tensile stress axis,following a plane of maximum shear stress.This type of shear fracture tends to minimize necking and avoids the triaxial state of stress that occurs in the necked region.

5.7.Bend test results

The bend tests for the welds joints were conducted mainly to assess the ductility and toughness of weldment.The face bend test samples of dissimilar EB welds before and after bend testing are shown in Fig.21(a)&(b).Fig.21(c)&(d)portrays the bend tested specimens of weld joints that possess highest and lowest breaking load respectively.The bend test specimens are prepared by machining the top depression and bottom penetration of both the weld joints.Face bend test of both the weld joints passed the 90°bend angle without resulting in any crack at the root.It is noticed from Fig.21(c)&(d)that the bending has shifted towards AA5083 alloy side as it has relatively lower strength and higher ductility as compared to the weld zone and AA2219 alloy base material.

通过6年的探索，中国药科大学在研究生国际化公开课建设方面取得了一定的成效，为国内药学类高校今后推进研究生教学课程国际化建设积累了经验，并发挥了一定的示范作用。

6.Conclusions

In the preset work,an in-depth comprehensive metallurgical characterization and the interaction effect of weld bead geometry over performance of electron beam weld joint of dissimilar aluminum alloys(AA2219 and AA5083)was studied.The following conclusions are drawn based on the results of the entire study.

1)Electron beam weld joints of good quality without bulk porosities may be produced over a wide range of welding parameters forthedissimilarcombination ofAA2219and AA5083 aluminium alloys.All the joints possess certain amount of top depression and positive penetration.

2)A mathematical model between the weld bead geometry(i.e.,topbead width,top depression,bottompenetration,and bottom bead width)and the tensile breaking load of weld joint is developed.The model can predict the tensile breaking load as a function of weld bead geometry as a with in an error of±10%.

3)The variation in welding parameters that increase the heat input,results in widening of top bead width,deepening of top depression as well as increases in bottom penetration.Weld bead geometry has a major in fluence on joint strength.Increased top bead width with minimum top depression and maximum bottom penetration leads to increase in effective thickness that in turn results in higher joint strength.

4)The electron beam welding produces very fine grains in fusion zone and softening in HAZ of AA5083 alloy.The key hole mode electron beam welding results in evaporation of magnesium from fusion zone.

5)Fusion interface close to AA5083 alloy has reduced hardness which can be correlated to the loss of cold working/softening due to decreased dislocation density due exposure to severe temperatures caused by welding heat input

6)The dissimilar weld joint possess the tensile breaking load moderately higher than AA5083 alloy base material and less than that of AA2219 alloy base material.The weld specimen has demonstrated better elongation than the specimen of AA2219 alloy base material and slightly lesser than the AA5083 alloy base material.The dissimilar electron beam weld has good bend ductility with major part of deformation existing in softer AA5083 alloy.

7)The failure location of dissimilar electron beam weld is affected by the weld bead geometry and the softening in fusion interface of AA5083 alloy.

自2016年4月24日开业，海吉星承接了马王堆蔬菜市场的整体搬迁后，物流园内每天都是车水马龙，人声鼎沸，一派繁忙景象。

Acknowledgements

The financial support from Defence Research and Development Organisation(DRDO)is greatly acknowledged.The authors are thankful to Shri.MSR Prasad,Director,Defence Research and Development Laboratory(DRDL)for his continued encouragement and for according permission to publish this work.

References

[1]Scultz H.Electron beam welding.Cambridge:Woodhead Publishing;2003.

[2]Bauer B,Busic M.High energy density welding process.EOLSS Publishers Co Ltd.https://www.eolss.net/Sample-Chapters/C05/E6-171-06-00.pdf.

[3]Metzer G,Lison R.Electron beam welding of dissimilar metals.Weld J Weld Res Suppl 1976:230s-40s.

[4]Sun Z,Karppi R.The application of electron beam welding for the joining of dissimilar metals:an overview.J Mater Process Technol 1996;59:257-67.

[5]Sharma A,Verma DK,Arora NA.Scheme of comprehensive assessment of weld bead geometry.Int J Adv Manuf Technol 2015;79:5-8.https://doi.org/10.1007/s00170-015-74520.

[6]Klykov NA,Dammer AA,Druzhinin AV,Malysh MM.Calculations of the form of the penetration zone in laser welding using a model of two heat sources.Weld Int 1987;1(10):914-6.

[7]Kumar C,Das M,Paul CP,Singh B.Experimental investigation and metallographic characterization of fiber laser beam welding of Ti-6Al-4V alloy using response surface method.Optic Laser Eng 2017;95:52-68.

[8]Siddaiah A,Singh BK,Mastanaiah P.Prediction and optimization of weld bead geometry for electron beam welding of AISI 304 stainless steel.Int J Adv Manuf Technol 2017.https://doi.org/10.1007/s00170-016 9046-x.

[9]Olshanskaya TV,Salomatova ES,Belenkiy VY,Trushnikov DN,Permyakov GL.Electron beam welding of aluminum alloy AlMg6 with a dynamically positioned electron beam.Int J Adv Manuf Technol 2016;89:3439-50.

[10]Kanigalpula PKC,Pratihar DK,Jha MN,Derose J,Bapat AV,Pal AR.Experimental investigations,input-output modeling and optimization for electron beam welding of Cu-Cr-Zr alloy plates.Int J Adv Manuf Technol 2015.https://doi.org/10.1007/s00170-015-7964-7.

[11]Kar J,Mahanty S,Roy SK,Roy GG.Estimation of average spot diameter and bead penetration using process model during electron beam welding of AISI 304 stainless steel.Int J Adv Manuf Technol 2015.https://doi.org/10.1007/s12666-015-0529-5.

[12]Dey V,Pratihar DK,Datta GL,Jha MN,Saha TK,Bapat AV.Optimization and prediction of weldment pro file in bead-on-plate welding of Al-1100 plates using electron beam.Int J Adv Manuf Technol 2010;48:513-28.https://doi.org/10.1007/s00170-009-2307-1.

[13]Montgomery DC.Design and analysis of experiments.eighth ed.Newyork:John Wiley&Sons Inc.;2013.

[14]Bo Li,Schen Y.The investigation of abnormal particle coarsening phenomena in Friction stir repair weld of AA2219-T6 aluminium alloy.Mater Des 2011;32:3796-802.

[15]Yan-bin C,Yu-gang M,Li-qun LI,Lin WU.Joint performance of laser-TIG double-side welded 5A06 aluminum alloy.Trans Nonferrous Metals Soc China 2009;19:26-31.

[16]Nair BS,Phanikumar G,Prasad Rao K,Sinha PP.Improvement of mechanical properties of gas tungsten arc and electron beam welded AA2219(Al-6 wt-%Cu)alloy.Sci Technol Weld Join 2007:579-85.

[17]Yamaguchi T,Kato M,Nishio K.Metallurgical characteristics of A5083-O aluminium alloyweldedbyhighenergydensitywelding.WeldInt 2010;13(9):712-20.

[18]Punkari A,Weckman DC,Kerr HW.Effects of magnesium content on dual beam Nd:YAG laser welding of Al-Mg alloys.Sci Technol Weld Join 2003;8:269-81.

[19]Cam G,Ventzke V,Santos JFD,Kocak M,Jennequin G,Gonthier-Maurin P.Characterisation of electron beam welded aluminium alloys.Sci Technol Weld Join 1999;4:317-23.

[20]Cam G,Ipekoglu G.Recent developments in joining of aluminum alloys.Int J Adv Manuf Technol 2016.https://doi.org/10.1007/s00170-016-9861-0.

[21]Mastanaiah P,Sharma A,Reddy GM.Dissimilar friction stir welds in AA2219-AA5083 aluminium alloys:effect of process parameters on material intermixing,defect formation,and mechanical properties.Trans Indian Inst Met 2016;69(7):1397-415.ISSN 0972-2815.

[22]Hetzberg RW.Deformation and fracture mechanics of Engineering materials.second ed.London:John Wiley&Sons Inc,London;1983.

[23]Oladimeji OO,Taban E.Trend and innovations in laser beam welding of wroughtaluminium alloys.WeldWorld2016.https://doi.org/10.1007/s40149-016-0317-9.